Two Component Black 5 Min. Repair Epoxy Putty (SF)

FOB Reference Price:Get Latest Price
24 Piece/Pieces (Min. Order)
Supply Ability:
20 Ton/Tons per Month
Port:
QINGDAO, SHANGHAI
Report Suspicious Activity
Overview
Quick Details
Other Names:
fast repair epoxy putty (SF)
Place of Origin:
Shandong, China (Mainland)
Classification:
Double Components Adhesives
Main Raw Material:
Epoxy
Usage:
Transportation, Automotive, industrial machinery, equipment, casting parts
Brand Name:
Darbond
Model Number:
1130
Color:
Dark Grey
Compressive strength:
105MPa
Tensile strength:
21MPa
Shear strength:
20
Hardness:
80D
Mixing Ratio (volume):
1:1
Mixing Ratio (weight):
1.7:1
Packaging & Delivery
Packaging Details
454g/set Item No. 113005
Delivery Time
15 days

Specifications

1. 5 min. repair putty
2. Can be machined after cured
3. Fast cures in 5 minutes
4. Designed for dependable emergency repair

Introduction

  Darbond® 5 min. repair putty 1130 is a two-component, room temperature curing epoxy adhesives. It is cold welding repairing materials filled with stainless steel powder and ceramic. Fast cures in 5 minutes. Suitable for emergency repairs of steel, stainless steel etc. damaged metal parts; wide application, easy to use, high bonding strength to substrate and can be used in low temperature conditions.

 

Typical Properties

  • Two component, paste.
  • Can be machined after cured.
  • Fast cures in 5 minutes, designed for dependable emergency repairs of steel, stainless steel fatigued metal parts in less than one hour.

 Typical Applications

  • Designed to emergently repair damaged, worn metal parts or stop leakage, such as steel, iron, stainless steel etc.
  • Also can be used to stop leakage of water supply and drainage metal pipeline.
  • Widely used for manufacture and maintenance of shipping, machinery, automotive and mining machinery etc.

  Datailed Products of Darbond® Metal Repair Putties

Product No.Typical UseUncured (After mixed)Cured
ColorCompressive Strength
GB/T1041-1992
Mpa
Tensile Strength
GB/T6329-1996
Mpa
Shear Strength
GB/T7124-1986
Mpa
Bending Strength
GB/T9341-2000
Mpa
Hardness
GB/T2411-1980
Shore D
Temperature Range
°C
11021Steel RepairGrey1253419-85-50-120
1103Aluminum casting repairAluminum983018-80-50-160
1104TBronze casting repairBronze953018-80-50-170
1105Stainless steel repairDark grey1053420-80-50-160
1126Wet surfaceBrown903118-80-50-150
1127High temperatureGrey893018-80-50-280
1128Oil levelLight yellow8820136785-50-150
1129Stopping leakage under pressureGrey9720133485-50-150
11305 Minutes cureDark grey1052120-80-50-120
CURING CONDITIONS
Product No.Mixture Ratio (A:B)Pot Life* minMinimum curing time before function   h
WeightVolume100g mixture50% load100% load
110219:14:1501018
11036:13.5:1601224
1104T9:13:1401224
110511:13.75:1501224
11265:13.5:120612
11273:12:180824
11281:11:1326
1129Knead after cutting420 min6
11301.7:11:1300.11
Note: * Temperature and mixture weight have great effect on pot life: below 15°C, curing speed is slow, it is recommended to heat; large mixture weight,           pot life will be shortened.
* Pot life means the time from mixing A, B component to dispensing to work parts.